Mae ASTM B111 yn safon ansawdd yn benodol ar gyfer tiwbiau trosglwyddo gwres a ddefnyddir mewn offer cyfnewid gwres. Mae'n nodi'r cyfansoddiad cemegol, priodweddau mecanyddol, goddefiannau dimensiwn, gofynion gweithgynhyrchu, a dulliau profi ar gyfer tiwbiau copr a aloi copr di-dor a ddefnyddir wrth gynhyrchu cyddwysyddion, anweddyddion, a chyfnewidwyr gwres eraill.
ASTM B111 Ystod Tiwbiau Copr
| Rhif UNS | Enw Cyffredin / Math o Ddeunydd | Cyfansoddiad enwol (pwysau %) |
|---|---|---|
| C10200 | Copr heb ocsigen | Cu 99.95% min |
| C12200 | Copr ffosfforized DHP | Cu 99.9% min, t 0.015-0.040% |
| C14200 | Copr ffosfforized, arsenical | Cu 99.7%, t 0.15-0.25%, fel 0.15-0.25% |
| C19200 | Copr ffosfforized, 1% haearn | Cu 99.78%, p 0.025%, Fe 0.80-1.20% |
| C23000 | Pres coch, 85% | Cu 84-86%, Zn 14-16% |
| C44300 | Pres Morlys, Arsenical | Cu 71-73%, Zn, SN 0.9-1.2%,Fel 0.02-0.06% |
| C44400 | Pres | Cu 71-73%, Zn, SN 0.9-1.2%,SB 0.02-0.10% |
| C44500 | Pres | Cu 71-73%, Zn, SN 0.9-1.2%,P 0.02-0.10% |
| C60800 | Efydd alwminiwm, 5% | Cu 91-93.5%, al 5.0-6.5%, Fe 1.0%ar y mwyaf |
| C61300 | Efydd alwminiwm, 7% | Cu 88.5-91.5%, AL 6.0-7.5%, Fe 2.0-3.0%, mn 0.5%ar y mwyaf |
| C61400 | Efydd alwminiwm, trwchus | Cu 88.5-91.5%, al 6.0-7.5%, Fe 1.5% ar y mwyaf, mn 1.0% ar y mwyaf |
| C68700 | Pres alwminiwm, arsenical | Cu 76-79%, Zn, AL 1.8-2.5%,Fel 0.02-0.06% |
| C70400 | Copr-nicel, 5% | Cu 94.5-95.5%, Ni 4.8-6.2%, Fe 1.3-1.7%, Mn 0.30-0.8% |
| C70600 | Copr-nicel, 10% | Cu 86.5% min, ni 9.0-11.0%, Fe 1.0-1.8%, mn 1.0% ar y mwyaf |
| C71000 | Copr-nicel, 20% | Cu 78.5-81.5%, NI 19.0-23.0%, Fe 0.50-1.0%, mn 1.0%ar y mwyaf |
| C71500 | Copr-nicel, 30% | Cu 65.0-70.2%, Ni 29.0-33.0%, Fe 0.40-1.0%, Mn 1.0%ar y mwyaf |
| C72200 | Copr-nicel, 16% cr | Cu 80.0-84.0%, Ni 15.0-17.5%, Fe 0.30%ar y mwyaf, cr 0.30-0.70% |
Cymhwyso Tiwbiau Copr ASTM B111
Mae cymhwyso tiwbiau aloi copr di-dor a gwmpesir gan safon ASTM B111 bron wedi'i ganoli ym maes cyfnewid gwres yn unig.
Diwydiant Pwer
Dyma'r ardal gais fwyaf a mwyaf hanfodol ar gyfer tiwbiau ASTM B111. Fe'i defnyddir yn bennaf yncyddwysyddion wynebo weithfeydd pŵer thermol a gorsafoedd pŵer niwclear. Yma, mae miloedd o diwbiau aloi copr yn cael eu bwndelu gyda'i gilydd i gyddwyso'r stêm wacáu yn gyflym o dyrbinau i mewn i ddŵr, a thrwy hynny greu a chynnal gwactod uchel wrth wacáu tyrbin. Mae'r broses hon yn hanfodol ar gyfer sicrhau effeithlonrwydd thermol y cylch cynhyrchu pŵer.
Peirianneg Forol ac Ar y Môr
Ar longau, defnyddir tiwbiau ASTM B111 yn helaeth mewn amrywiol offer cyfnewid gwres, gan gynnwysPrif Oeri Peiriant, Oeryddion olew iro, Systemau Oeri Canolog, aanweddyddion ar gyfer planhigion dihalwyno. Mae'r unedau offer hyn yn defnyddio dŵr y môr yn uniongyrchol fel y cyfrwng oeri, gan arwain at amgylchedd gweithredu hynod heriol. Felly, rhaid i'r tiwbio feddu ar wrthwynebiad eithriadol icyrydiad dŵr y môraerydiad cavitationi sicrhau gweithrediad dibynadwy tymor hir yr offer.
Prosesau petrocemegol a diwydiannol
Mewn purfeydd, planhigion cemegol, a diwydiannau prosesu eraill, mae nifer o brosesau diwydiannol yn cynhyrchu gwres sylweddol y mae angen eu cyfnewid yn amserol. Defnyddir tiwbiau ASTM B111 i gynhyrchu amrywioloeri prosesu, anweddyddion, aailbyllau. Fe'u defnyddir i oeri hylifau proses poeth neu ddarparu ffynhonnell wres ar gyfer offer fel colofnau distyllu.
HVAC & R (gwresogi, awyru, aerdymheru a rheweiddio)
Mewn systemau aerdymheru canolog mawr ac unedau rheweiddio diwydiannol, gellir defnyddio tiwbiau ASTM B111 ynanweddyddion cregyn a thiwbacyddwysyddion. Er ei fod yn wynebu cystadleuaeth o ddeunyddiau fel dur gwrthstaen neu ditaniwm yn y maes hwn, mae aloion copr yn dal i ddal lle mewn llawer o gymwysiadau oherwydd eu dargludedd thermol cyfun a'u cost-effeithiolrwydd, yn enwedig wrth drin cyfryngau dŵr glân neu wedi'u trin.
Cyfansoddiad cemegol aloion copr yn ASTM B111
| Rhif UNS | Enw cyffredin | Cu | Zn | Sn | PB (Max) | Fe (Max) | NI (Max) | Han | MN (Max) | Elfennau eraill |
|---|---|---|---|---|---|---|---|---|---|---|
| C10200 | Copr heb ocsigen | 99.95 | - | - | 0.005 | - | - | - | - | O: 0.0015 ar y mwyaf |
| C12200 | Copr DHP | 99.9 | - | - | 0.05 | 0.05 | 0.05 | - | - | P: 0.015-0.040 |
| C14200 | Cu ffosfforized, fel | 99.7 | - | - | 0.05 | 0.05 | 0.05 | - | - | P: 0.10-0.25; UG: 0.15-0.25 |
| C19200 | Cu ffosfforized, 1% Fe | 99.78 | - | - | 0.05 | 0.80-1.20 | 0.20 | - | 0.10 | P: 0.025-0.050 |
| C23000 | Pres Coch | 84.0 | Gweddillion | - | 0.05 | 0.05 | 0.6 | - | - | - |
| C44300 | Morlys, arsenical | 71.0 | Gweddillion | 0.9-1.2 | 0.07 | 0.06 | 0.7 | - | - | UG: 0.02-0.06 |
| C44400 | Morlys, antimonial | 71.0 | Gweddillion | 0.9-1.2 | 0.07 | 0.06 | 0.7 | - | - | SB: 0.02-0.10 |
| C44500 | Morlys, ffosfforized | 71.0 | Gweddillion | 0.9-1.2 | 0.07 | 0.06 | 0.7 | - | - | P: 0.02-0.10 |
| C60800 | Efydd alwminiwm, 5% | 91.0 | - | - | 0.05 | 1.0 | 0.5 | 5.0-6.5 | 0.50 | - |
| C61300 | Efydd alwminiwm, 7% | 88.5 | - | - | 0.05 | 2.0-3.0 | 0.25 | 6.0-7.5 | 0.50 | - |
| C61400 | Efydd alwminiwm, trwchus | 90.0 | - | - | 0.05 | 1.5 | 0.25 | 6.0-7.5 | 1.0 | - |
| C68700 | Pres alwminiwm, arsenical | 76.0 | Gweddillion | - | 0.07 | 0.06 | 0.5 | 1.8-2.5 | 0.50 | UG: 0.02-0.10 |
| C70400 | Cu-ni, 5% | 94.5 | 1.0 | - | 0.05 | 1.3-1.7 | 4.8-6.2 | - | 0.30-0.8 | - |
| C70600 | Cu-ni, 10% | 86.5 | 1.0 | - | 0.05 | 1.0-1.8 | 9.0-11.0 | - | 1.0 | - |
| C71000 | Cu-ni, 20% | 78.5 | 1.0 | - | 0.05 | 0.50-1.0 | 19.0-23.0 | - | 1.0 | - |
| C71500 | Cu-ni, 30% | 65.0 | 1.0 | - | 0.05 | 0.40-1.0 | 29.0-33.0 | - | 1.0 | - |
| C72200 | Cu-ni, 16% cr | 80.0 | 0.5 | - | 0.02 | 0.30 | 15.0-17.5 | - | 0.70 | CR: 0.30-0.70 |
Priodweddau mecanyddol aloion copr yn ASTM B111
| Rhif UNS | Themprem | Cryfder tynnol Min (KSI) [MPA] | Cryfder cynnyrch (0.5% est) min (ksi) [mpa] | Elongation min (% mewn 2 i mewn) | Caledwch Rockwell (nodweddiadol) |
|---|---|---|---|---|---|
| C10200 | O60 (Annealed) | 25 [170] | - | 40 | F40 (HRF) |
| C12200 | O61 (Annealed) | 28 [195] | - | 40 | F50 (HRF) |
| C14200 | O61 (Annealed) | 30 [205] | 10 [70] | 35 | F55 (HRF) |
| C19200 | O61 (Annealed) | 36 [250] | 10 [70] | 35 | B45 (HRB) |
| C23000 | O61 (Annealed) | 40 [275] | 12 [80] | 35 | B50 (HRB) |
| C44300 | O61 (Annealed) | 47 [325] | 18 [125] | 45 | B65 (HRB) |
| C44400 | O61 (Annealed) | 47 [325] | 18 [125] | 45 | B65 (HRB) |
| C44500 | O61 (Annealed) | 47 [325] | 18 [125] | 45 | B65 (HRB) |
| C60800 | O61 (Annealed) | 50 [345] | 20 [140] | 35 | B70 (HRB) |
| C61300 | O61 (Annealed) | 65 [450] | 25 [170] | 30 | B80 (HRB) |
| C61400 | O61 (Annealed) | 60 [415] | 22 [150] | 35 | B75 (HRB) |
| C68700 | O61 (Annealed) | 50 [345] | 20 [140] | 35 | B70 (HRB) |
| C70400 | O61 (Annealed) | 38 [260] | 12 [80] | 35 | B45 (HRB) |
| C70600 | O61 (Annealed) | 44 [305] | 16 [110] | 35 | B60 (HRB) |
| C71000 | O61 (Annealed) | 52 [360] | 20 [140] | 35 | B70 (HRB) |
| C71500 | O61 (Annealed) | 60 [415] | 25 [170] | 35 | B80 (HRB) |
| C72200 | O61 (Annealed) | 50 [345] | 22 [150] | 35 | B70 (HRB) |
Goddefiannau dimensiwn ar gyfer tiwbiau aloi copr yn ASTM B111
1. Goddefiannau diamedr y tu allan (OD)
| Y tu allan i ddiamedr (mewn) | Oddefgarwch |
|---|---|
| Hyd at 1/2 | ±0.002 |
| Dros 1/2 i 3/4 | ±0.0025 |
| Dros 3/4 i 7/8 | ±0.003 |
| Dros 7/8 i 1 | ±0.0035 |
| Dros 1 i 1 1/4 | ±0.004 |
| Dros 1 1/4 i 1 1/2 | ±0.0045 |
| Dros 1 1/2 i 2 | ±0.005 |
| Dros 2 i 2 1/2 | ±0.006 |
| Dros 2 1/2 i 3 | ±0.007 |
| Dros 3 i 4 | ±0.008 |
| Dros 4 i 5 | ±0.010 |
| Dros 5 i 6 | ±0.012 |
| Dros 6 i 7 | ±0.014 |
| Dros 7 i 8 | ±0.016 |
2. Goddefiannau trwch wal
| Thrwch wal | Oddefgarwch |
|---|---|
| Hyd at 0.030 | ±10% |
| Dros 0.030 i 0.040 | ±9% |
| Dros 0.040 i 0.050 | ±8% |
| Dros 0.050 i 0.060 | ±7% |
| Dros 0.060 i 0.080 | ±6% |
| Dros 0.080 i 0.100 | ±5% |
| Dros 0.100 | ±4% |
3. Goddefiannau hyd ar gyfer tiwbiau hyd syth
| Hyd (tr) | Oddefgarwch |
|---|---|
| Hyd at 12 | +1/8, -0 |
| Dros 12 i 22 | +3/16, -0 |
| Dros 22 i 28 | +1/4, -0 |
| Dros 28 i 35 | +5/16, -0 |
| Dros 35 | +3/8, -0 |
4. Goddefgarwch Syth
| Hyd (tr) | Y gwyriad uchaf oddi wrth sythrwydd (IN) |
|---|---|
| Hyd at 12 | 1/16 |
| Dros 12 i 22 | 3/32 |
| Dros 22 i 28 | 1/8 |
| Dros 28 i 35 | 5/32 |
| Dros 35 | 3/16 |
Planhigyn ac offer
Pecynnu a Llongau
Ymweliadau cwsmeriaid
Fel menter broffesiynol sy'n ymroddedig i fasnach cynnyrch copr byd -eang er 2008, mae Gnee Metal Group yn cydnabod yn ddwfn yr ansawdd a'r cyfrifoldeb a ymgorfforir yn safon ASTM B111. Mae'r safon hon nid yn unig yn nodi cyfansoddiad cemegol ac eiddo mecanyddol ond mae hefyd yn cynrychioli ymrwymiad ansawdd cynhwysfawr sy'n rhychwantu prosesau gweithgynhyrchu i brofi a gwirio. Mae Gnee yn sicrhau cwsmeriaid byd-eang yn ddifrifol y bydd pob tiwb cyddwysydd ASTM B111-safonol a thiwb aloi copr yr ydym yn eu cyflenwi yn cadw'n llwyr at ei ofynion ar gyfer gweithgynhyrchu di-dor, anelio triniaeth, profion cyfredol eddy, a phrofion perfformiad mecanyddol amrywiol. Mae hyn yn sicrhau bod ein cynhyrchion yn darparu ymwrthedd cyrydiad eithriadol a pherfformiad trosglwyddo gwres dibynadwy mewn cymwysiadau beirniadol fel gweithfeydd pŵer, adeiladu llongau, a phrosesu cemegol.
Cysylltwch â ni heddiw i gael dyfynbris:sales@gneesteel.com
Tagiau poblogaidd: ASTM B111 Tiwbiau Copr, China ASTM B111 Tiwbiau Copr Gwneuthurwyr, Cyflenwyr, Ffatri
Nesaf
JumboFe allech Chi Hoffi Hefyd
Anfon ymchwiliad